The performance of superconducting qubits is often limited by dissipation and two-level systems (TLS) losses. The dominant sources of these losses are believed to originate from amorphousmaterials and defects at interfaces and surfaces, likely as a result of fabrication processes or ambient exposure. Here, we explore a novel wet chemical surface treatment at the Josephson junction-substrate and the substrate-air interfaces by replacing a buffered oxide etch (BOE) cleaning process with one that uses hydrofluoric acid followed by aqueous ammonium fluoride. We show that the ammonium fluoride etch process results in a statistically significant improvement in median T1 by ∼22% (p=0.002), and a reduction in the number of strongly-coupled TLS in the tunable frequency range. Microwave resonator measurements on samples treated with the ammonium fluoride etch prior to niobium deposition also show ∼33% lower TLS-induced loss tangent compared to the BOE treated samples. As the chemical treatment primarily modifies the Josephson junction-substrate interface and substrate-air interface, we perform targeted chemical and structural characterizations to examine materials‘ differences at these interfaces and identify multiple microscopic changes that could contribute to decreased TLS.
We present a novel transmon qubit fabrication technique that yields systematic improvements in T1 coherence times. We fabricate devices using an encapsulation strategy that involvespassivating the surface of niobium and thereby preventing the formation of its lossy surface oxide. By maintaining the same superconducting metal and only varying the surface structure, this comparative investigation examining different capping materials and film substrates across different qubit foundries definitively demonstrates the detrimental impact that niobium oxides have on the coherence times of superconducting qubits, compared to native oxides of tantalum, aluminum or titanium nitride. Our surface-encapsulated niobium qubit devices exhibit T1 coherence times 2 to 5 times longer than baseline niobium qubit devices with native niobium oxides. When capping niobium with tantalum, we obtain median qubit lifetimes above 200 microseconds. Our comparative structural and chemical analysis suggests that amorphous niobium suboxides may induce higher losses. These results are in line with high-accuracy measurements of the niobium oxide loss tangent obtained with ultra-high Q superconducting radiofrequency (SRF) cavities. This new surface encapsulation strategy enables further reduction of dielectric losses via passivation with ambient-stable materials, while preserving fabrication and scalable manufacturability thanks to the compatibility with silicon processes.
Continued advances in superconducting qubit performance require more detailed understandings of the many sources of decoherence. Within these devices, two-level systems arise due todefects, interfaces, and grain boundaries, and are thought to be a major source of qubit decoherence at millikelvin temperatures. In addition to Al, Nb is a commonly used metalization layer for superconducting qubits. Consequently, a significant effort is required to develop and qualify processes that mitigate defects in Nb films. As the fabrication of complete superconducting qubits and their characterization at millikelvin temperatures is a time and resource intensive process, it is desirable to have measurement tools that can rapidly characterize the properties of films and evaluate different treatments. Here we show that measurements of the variation of the superconducting critical temperature Tc with an applied external magnetic field H (of the phase boundary Tc−H) performed with very high resolution show features that are directly correlated with the structure of the Nb films. In combination with x-ray diffraction measurements, we show that one can even distinguish variations quality and crystal orientation of the grains in a Nb film by small but reproducible changes in the measured superconducting phase boundary.
Niobium thin films on silicon substrate used in the fabrication of superconducting qubits have been characterized using scanning and transmission electron microscopy, electrical transport,magnetization, quasiparticle spectroscopy, and real-space real-time magneto-optical imaging. We study niobium films to provide an example of a comprehensive analytical set that may benefit superconducting circuits such as those used in quantum computers. The films show outstanding superconducting transition temperature of Tc=9.35 K and a fairly clean superconducting gap, along with superfluid density enhanced at intermediate temperatures. These observations are consistent with the recent theory of anisotropic strong-coupling superconductivity in Nb. However, the response to the magnetic field is complicated, exhibiting significantly irreversible behavior and insufficient heat conductance leading to thermo-magnetic instabilities. These may present an issue for further improvement of transmon quantum coherence. Possible mitigation strategies are discussed.
This white paper presents a single-layer mask, found at this https URL. It is designed for fabrication of superconducting microwave resonators towards 1:1 comparisons of dielectriclosses from the metal-substrate interface. Finite-element electromagnetic simulations are used to determine participation ratios of the four major regions of the on-chip devices, as well as to confirm lack of crosstalk between neighboring devices and demonstrate coupling tunability over three orders of magnitude. This mask is intended as an open-source community resource for facilitating precise and accurate comparisons of materials in the single-photon, millikelvin regime.